Introduction
Super alloys or high performance alloys are available in a variety of shapes and contain elements in different combinations to obtain a specific result. These alloys are of three types that include iron-based, cobalt-based and nickel-based alloys. The nickel-based and cobalt-based super alloys are available as cast or wrought based alloys according to composition and application.
Super alloys have good oxidation and creep resistance and can be strengthened by precipitation hardening, solid-solution hardening and work hardening methods. They can also function under high mechanical stress and high temperatures and also in places that require high surface stability.
HASTELLOY(r) C276 is a wrought corrosion-resistant alloy that resists the development of grain boundary precipitates that degrade corrosion resistance.
The following datasheet provides an overview of HASTELLOY(r) C276.
Chemical Composition
The chemical composition of HASTELLOY(r) C276 is outlined in the following table.
| Element | Content (%) |
|---|---|
| Nickel, Ni | 57 |
| Molybdenum, Mo | 15-17 |
| Chromium, Cr | 14.5-16.5 |
| Iron, Fe | 4-7 |
| Tungsten, W | 3-4.50 |
| Cobalt, Co | 2.50 |
| Manganese, Mn | 1 |
| Vanadium, V | 0.35 |
| Silicon, Si | 0.080 |
| Phosphorous, P | 0.025 |
| Carbon, C | 0.010 |
| Sulfur, S | 0.010 |
Physical Properties
The following table shows the physical properties of HASTELLOY(r) C276.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm³ | 0.321 lb/in³ |
| Melting point | 1371°C | 2500°F |
Mechanical Properties
The mechanical properties of HASTELLOY(r) C276 are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (@thickness 4.80-25.4 mm, 538°C/@thickness 0.189-1.00 in, 1000°F) | 601.2 MPa | 87200 psi |
| Yield strength (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F) | 204.8 MPa | 29700 psi |
| Elastic modulus (RT) | 205 GPa | 29700 ksi |
| Elongation at break (in 50.8 mm, @thickness 1.60-4.70 mm, 204°C/@thickness 0.0630-0.185 in, 399°F) | 56% | 56% |
| Hardness, Rockwell B (plate) | 87 | 87 |
Thermal Properties
The thermal properties of HASTELLOY(r) C276 are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@24-93°C/75.2-199°F) | 11.2 µm/m°C | 6.22 µin/in°F |
| Thermal conductivity (-168 °C) | 7.20 W/mK | 50.0 BTU in/hr.ft².°F |
Other Designations
Equivalent materials to HASTELLOY(r) C276 are as follows.
| ASTM B366 | ASTM B574 | ASTM B622 | ASTM F467 | DIN 2.4819 |
| ASTM B575 | ASTM B626 | ASTM B619 | ASTM F468 |
Post time: Jul-03-2023